①.《工(gong)(gong)業金屬管(guan)(guan)(guan)(guan)道設(she)計規(gui)范》GB50316對焊(han)(han)后熱(re)處(chu)(chu)理(li)的(de)(de)規(gui)定(ding)(ding)：a. 碳鋼管(guan)(guan)(guan)(guan)道壁厚(hou)(hou)(hou)大(da)于(yu)或(huo)等于(yu)19mm時(shi)應(ying)(ying)進(jin)行焊(han)(han)后熱(re)處(chu)(chu)理(li)；b. 管(guan)(guan)(guan)(guan)道焊(han)(han)后需熱(re)處(chu)(chu)理(li)的(de)(de)管(guan)(guan)(guan)(guan)道厚(hou)(hou)(hou)度：管(guan)(guan)(guan)(guan)道焊(han)(han)后需要(yao)熱(re)處(chu)(chu)理(li)的(de)(de)厚(hou)(hou)(hou)度及要(yao)求除按GB50316的(de)(de)規(gui)定(ding)(ding)外，還應(ying)(ying)符(fu)合《現場設(she)備、工(gong)(gong)業管(guan)(guan)(guan)(guan)道焊(han)(han)接(jie)工(gong)(gong)程施工(gong)(gong)規(gui)范》GB50235、《工(gong)(gong)業金屬管(guan)(guan)(guan)(guan)道工(gong)(gong)程施工(gong)(gong)質量驗收規(gui)范》GB50184的(de)(de)規(gui)定(ding)(ding)；c. 當材料含碳量高于(yu)時(shi)任何(he)壁厚(hou)(hou)(hou)均宜進(jin)行焊(han)(han)后熱(re)處(chu)(chu)理(li)；d. 當管(guan)(guan)(guan)(guan)子(zi)或(huo)管(guan)(guan)(guan)(guan)件采用焊(han)(han)接(jie)連接(jie)時(shi)，推薦的(de)(de)預熱(re)和熱(re)處(chu)(chu)理(li)要(yao)求所采用的(de)(de)厚(hou)(hou)(hou)度，應(ying)(ying)是連接(jie)接(jie)頭處(chu)(chu)的(de)(de)較厚(hou)(hou)(hou)的(de)(de)壁厚(hou)(hou)(hou)，但需注意規(gui)范規(gui)定(ding)(ding)的(de)(de)除外情(qing)況(kuang)。

  ②.《天然氣凈化處理廠設計(ji)規(gui)范》SY/T 0011的6.3.10條(tiao)規(gui)定：在酸性環(huan)境中使用的碳鋼(gang)管道及設備應進行焊后熱處理。

  ③.《石油天然氣(qi)建設工程(cheng)施工質量驗收規(gui)范天然氣(qi)凈化處(chu)(chu)理(li)廠工程(cheng)》SY 4209 中(zhong)說明含量大于5％的焊縫熱(re)處(chu)(chu)理(li)后要進行硬度檢查。未(wei)明確(que)＜5％的情(qing)況，未(wei)明確(que)熱(re)處(chu)(chu)理(li)工藝要求。

  ④.《現(xian)場設備(bei)、工(gong)(gong)業(ye)管(guan)道焊(han)接工(gong)(gong)程(cheng)施(shi)工(gong)(gong)規范》GB 50236 中僅(jin)對壁厚大于30mm的有溫度要求，而薄壁管(guan)未有要求及做(zuo)法(fa)。

  ⑤. SH／T 3059規定以(yi)下情況需要焊(han)后熱處理。

   a. 在濕H₂S應力腐蝕環境中，壓力管道需經焊后熱處理，熱處理后焊縫（含熱影響區）的硬度不大于200HB。

   b. 在液氨應力腐蝕環境(jing)中，使用低(di)碳鋼和低(di)合(he)金(jin)高(gao)強(qiang)度鋼（包括焊接(jie)接(jie)頭）。對于Q235-A、Q235-B、Q235-C、20、16Mn鋼，焊后(hou)應進行消(xiao)除應力熱處理。對于15MnV、18MnMoNb低(di)合(he)金(jin)高(gao)強(qiang)度鋼，焊后(hou)必(bi)須進行消(xiao)除應力熱處理。